hi, the blockwork was left for 28 days (webers specification) before the render was applied, like i've said, this problem has never occured before and im putting it down to the fact that the new maxit, manufactured by weber is nothing short of sh*te, cheers for your input though!
never used mesh before, so didnt feel it wes necessary to start using it now(never had maxit mq, r or rg crack before either) my judgement on the substrate im applying onto has always stood me in good stead, this time i cant help but feeling that weber dont give a toss about the lads that are...
hi all, this job has recently turned a corner and is now cracking on the new block-work aswell, i've had the weber rep back out to it and have been informes today that its cracking because the blocks are the wrong kilo-newtons(ive never heard so much bollox in my life) if anybody else is having...
my thoughts exactly! try getting the weber reps to admit it though! what renders are you using now? i really dont want to stop the coloured render side of things, i love the outside work, any feedback/links would be much appreciated, cheers.
its on existing render,(100% solid) used rend-aid first then applied to spec, was wondering if anyone else had noticed how sh*te maxit has gone since weber started to manufacture it! ive used the stuff for years and never had problems before,
hi, ive been using one coat renders for about 12 years, switched from weber to maxit about 4 years ago, maxit have just been bought out and the first job ive done with the irish maxit is cracking all over the place, its been applied the same way as i've always done it, and i've never had...