That's what the architect spect. I wanted to do it in hardwall. I'm really trying to establish if Pva solution would cause failure in bond. Thankfully the walls doesn't sound hollow when you tap them.
Getting slot of hairline cracks in the skim work and am trying to get to the root cause. It was noted that the blocks were not ideal as had no key. Usually I'd just dampen down the blockwork so instead i put solution over it and went on when tacky. Trying to find out if solution was a bad idea.